Mieszaniny uwodornionego i karboksylowanego kauczuku butadienowo-akrylonitrylowego - sieciowanie i wybrane właściwości

K. Bociong; W. M. Rzymski

Published : 2022-08-18

Vol. 54 No. 5 (2009)

Blends of hydrogenated and carboxylated acrylonitrile-butadiene rubber - curing and selected properties

K. Bociong W. M. Rzymski

Abstract

Hydrogenated and carboxylated acrylonitrile-butadiene rubbers (HNBR and XNBR, respectively) were blended in various ratios by reactive mixing and then the compositions were subjected to selective dynamic curing with use of MgO and subsequent static curing of the whole system with dicumyl peroxide (DCP). The effects of XNBR content in the blend, curing agents added and dispergation time on the properties of vulcanizates obtained were investigated. It was found that during the dynamic curing of XNBR in the blend with HNBR the change in morphology occurred: with two co-continuous phases to mixed partially lamellar, rod-like and droplet ones (Fig. 1). Curing degree of the composition, calculated on the basis of equilibrium swelling (Vr) measurements and elasticity constants 2C1, increase with increasing XNBR content in the system (Fig. 2, 3). Tensile strength (TSb) and elongation at break (Eb) depend on the components' dispergation time and process conditions (Fig. 5-10).

Keywords

reaktywne przetwórstwo ; dynamiczna wulkanizacja ; uwodorniony kauczuk butadienowo-akrylonitrylowy ; karboksylowany kauczuk butadienowo-akrylonitrylowy reactive processing ; dynamic vulcanization ; hydrogenated acrylonitrile-butadiene rubber ; carboxylated acrylonitrile-butadiene rubber

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Bociong, K., & Rzymski, W. M. (2022). Blends of hydrogenated and carboxylated acrylonitrile-butadiene rubber - curing and selected properties. Polimery, 54(5), 370–376. Retrieved from https://polimery.ichp.vot.pl/index.php/p/article/view/1211

References

Beniska J., Kisela G., Rosner R: Polimery 1985,30,432.

2. Rzymski W. M.: Polimery 1999, 44,505.

3. Radusch H. J., Rzymski W. M.: Polimery 2002,47,229.

4. Rzymski W. M.: Polimery 1991,36,409.

5. Radusch H. J., Rzymski W. M.: Elastomery 2001, 5, (nr 2), 3.

6. Rzymski W. M., Kozioł M.: „Kohäsionseigenschaften von karboxylierten Nitrilkautschuken", w Mat. Konf: Intern. Conf. „Polymerwerkstoffe-2006 ", Halle 2006, P-62.

7. Rzymski W. M., Smejda-Krzewicka A.: e-Polymers 2005, P_073.

8. Kozioł M., Rzymski W. M., Maćkowska A.: e-Polymers 2006,P_011.

9. Smejda-Krzewicka A., Rzymski W. M.: Polimery 2006, 51, 66.

10. Radusch H. J., Rzymski W. M.: Polimery 2005, 50,249.

11. Rzymski W. M., Radusch H. J.: Elastomery 2001, 5, (nr 2), 19.

12. Rzymski W. M.: Polimery 1997, 42,450.

13. Radusch H. J., Pham T.: Kautsch. Gummi Kunstst. 1996, 49, 249.

14. Praca zbiorowa: „Thermoplastic Elastomers from Rubber-Plastic Blends", (red. De S. K., Bhowmick A.K.), Ellis Horwood Publishers, New York 1990, str, 265.

15. Łupke Th., Radusch H. J.: Kautsch. Gummi Kunstsl 1992,45,91.

16. Rzymski W. M., Kmiotek M.: Polimery 2007, 52,511.

17. Wojtyra K., Rzymski W. M.: w pracy zbiorowej: „Modyfikacja Polimerów. Stan i perspektywy w roku 2007 " (red. Steller R., Żuchowska D.), Oficyna Wyd, Politechniki Wrocławskiej, Wrocław 2007, str. 213—218.

Google Scholar

Altmetric indicators

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0