Wpływ poli(tereftalanu butylenu) funkcjonalizowanego 2,2'-(1,3-fenyleno)-bis(2-oksazoliną) na strukturę i właściwości mieszanin poliamidu 6 z odpadami włókienniczymi zawierającymi poli(tereftalan etylenu)

R. Jeziórska

Published : 2022-08-24

Vol. 53 No. 3 (2008)

Effect of poly(butylene terephthalate) functionalized with 2,2'-(1,3-phenylene)-bis(2-oxazoline) on the structure and properties of polyamide 6 blends with textile waste containing poly(ethylene terephthalate)

R. Jeziórska

Abstract

The blends of polyamide 6 (PA6, 65 wt. parts), textile waste containing poly(ethylene terephthalate) (PET, 35 wt. parts, Table 1) with poly(butylene terephthalate) (PBT) functionalized with 2,2'-(1,3-phenylene)-bis(2-oxazoline) (PBO) were prepared using a co-rotating twin-screw extruder. The effects of a presence and amount of PBT - PBO on thermal properties (Table 2) and phase structures of the blends obtained (Table 3) were investigated by differential scanning calorimetry (Fig. 1), scanning electron microscopy (Fig. 2 and 3) and selective solubility in formic acid (Table 4). The blends show heterogenic structures stabilized at microphase level. This is a result of chemical reactions going during the extrusion process (probably the reactions of PA and PET functional groups with oxazoline groups built-in into PBT [equation (1), (3) and (4)]. PBT - PBO presence improves the mechanical and processing properties of the blends (Table 5-7). The results of investigations show the compatibilizing effect of PBO.

Keywords

mieszaniny PA/PET ; 2,2'-(1,3-fenyleno)-bis(2-oksazolina) ; kompatybilizacja ; struktura ; właściwości cieplne ; właściwości mechaniczne PA/PET blends ; 2,2'-(1,3-phenylene)-bis(2-oxazoline) ; compatibilization ; structure ; thermal properties ; mechanical properties

Similar Articles

H. Kaczmarek, R. Czajka, M. Nowicki, M. Wiśniewski, Polymer studies using atomic force microscopy (AFM). Part II. Investigation of chemical reactions and physical processes in polymers , Polimery: Vol. 48 No. 2 (2003)
J. Polaczek, E. Dziki, J. Pielichowski, Properties and synthesis of poly(aspartic acid) and its derivatives , Polimery: Vol. 48 No. 1 (2003)
Z. Urbańczyk-Lipkowska, J. Janiszewska, Organometallic dendrimers - molecular architecture and functions , Polimery: Vol. 48 No. 1 (2003)
A. Jabłonowska, M. Dadlez, A beta peptide oligomers - potential neurotoxic agents in Alzheimer's disease , Polimery: Vol. 48 No. 1 (2003)
E. Kowalska, Z. Wielgosz, M. Żubrowska, S. Pasynkiewicz, M. Choroś, Application of waste phosphogypsum in thermoplastic and chemosetting composites , Polimery: Vol. 49 No. 11-12 (2004)
J. Pielichowski, P. Penczek, D. Bogdal, E. Wolff, J. Gorczyk, Microwave assisted synthesis of unsaturated polyester resins , Polimery: Vol. 49 No. 11-12 (2004)
A. Wojtala, W. Herzog, K. Czaja, Modification of low density polyethylene with allylurea , Polimery: Vol. 49 No. 10 (2004)
H. Maciejewski, I. Dąbek, B. Marciniec, Silane coupling agents. Part IX. Epoxyfunctional carbosilanes , Polimery: Vol. 49 No. 10 (2004)
K. Piszczek, J. Tomaszewska, T. Sterzyński, The universal temperature parameter of rigid PVC gelation in Brabender kneader , Polimery: Vol. 49 No. 9 (2004)
W. Zatorski, Z. K. Brzozowski, K. Łebek, Production of PUR and PUR-PIR foams with red phosphorus as a flame retardant , Polimery: Vol. 50 No. 9 (2005)

<< < 119 120 121 122 123 124

You may also start an advanced similarity search for this article.

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Jeziórska, R. (2022). Effect of poly(butylene terephthalate) functionalized with 2,2’-(1,3-phenylene)-bis(2-oxazoline) on the structure and properties of polyamide 6 blends with textile waste containing poly(ethylene terephthalate). Polimery, 53(3), 201–207. Retrieved from https://polimery.ichp.vot.pl/index.php/p/article/view/1302

References

Praca zbiorowa: „Handbook of Plastics Recycling” (red. La Mantia F.), Rapra Technology Limited, Shrewsbury UK 2002.

2. Zdrazilowa N., Hausnerova B., Kitano T., Saha P.: Polimery 2004, 49, 819.

3. Darie R. N., Vasile C., Kozłowski M.: Polimery 2006, 51, 656.

4. Jeziórska R.: Polym. Degrad. Stab. 2005, 90, 224.

5. Jeziórska R.: Pigm. Res. Technol. 2006, 35, 3.

6. Jeziórska R.: Polimery 2007, 52, 294.

7. Jeziórska R.: Polimery 2007, 52, 371.

8. Jeziorska R., Wielgosz Z.: Przem. chem. 2007, 86, 291.

9. Shyichuk A., Piszczek K., Rokitnicka J.: Polimery 2006, 51, 382.

10. Kowalska E., Kuczyńska L., Wielgosz Z., Choroś M.: Polimery 2006, 51, 576.

11. Pińkowska H.: Polimery 2006, 51, 836.

12. Jana G. K., Mahaling R. N., Rath T., Kozłowska A., Kozłowski M., Das Ch. K.: Polimery 2007, 52, 131.

13. Maridass B., Gupta B. R.: Polimery 2007, 52, 456.

14. Praca zbiorowa: „Reactive modifiers for polymer blends” (red. Al Malaika S.). Blackie Academic & Professional, London 1997.

15. Xanthos M., Dagli S. S.: Polym. Eng. Sci. 1991, 31, 929.

16. Jeziorska R., Wielgosz Z.: Przem. chem. 2002, 81, 785.

17. Xanthos M.: „Reactive extrusion”. Oxford University Press, New York 1992.

18. Alexandre M., Dubois P.: Mater. Sci. Eng. 2000, 28, 1.

19. Giannelis E. P. i in.: Adv. Polym. Sci. 1999, 118, 108.

20. Messersmith P. B., Giannelis E. P.: Chem. Mater. 1994, 6, 1719.

21. Fisher H. R., Gielgens L. H., Koster T. P. M.: Acta Polym. 1999, 50, 122.

22. Le Pluart L., Duchet J., Sautereau H., Gerard J. F.: Macromol. Symp. 2003, 194, 155.

23. Wagenknecht U., Kretzschmar B., Reinhardt G.: Macromol. Symp. 2003, 194, 207.

24. Jeziórska R.: Polimery 2003, 48, 130.

25. Jeziórska R.: Polimery 2004, 49, 350.

26. Jeziórska R.: Polimery 2004, 49, 47.

27. Jeziórska R.: Polimery 2005, 50, 291.

28. Jeziórska R.: Polimery 2005, 50, 468.

29. Jeziórska R.: „Studium procesu wytłaczania reaktywnego”, Wydawnictwa Uczelniane, Lublin 2005.

30. Jeziórska R.: Polimery 2006, 51, 351.

31. Zgł. Pat. Pol. P-349 968 (2001).

32. Saechtling H., Zebrowski W.: „Tworzywa sztuczne -- Poradnik”, Wydawnictwa Naukowo-Techniczne, Warszawa 1978.

33. Sikora R.: „Przetwórstwo tworzyw wielkocząsteczkowych”, Wydawnictwo Edukacyjne, Warszawa 1993.

34. Cheng S. Z. D.: J. Appl. Polym. Symp. 1989, 43, 315.

35. Instrukcja obsługi aparatu DSC-2-PERKIN-ELMER, Norwalk, Connecticut, USA 1978.

36. Wunderlich B.: “Macromolecular Physics”, tom I, Academic Press INC, New York--London 1973, str. 401--404.

37. Galina H.: „Fizykochemia polimerów”, Oficyna Wydawnicza Politechniki Rzeszowskiej, Rzeszów 1998, str. 180.

38. Mehta A., Gaur U., Wunderlich B.: J. Polym. Sci.: Polym. Phys. Ed. 1978, 16, 289.

39. Wunderlich B.: „Thermal Analysis“, Academic Press, New York 1990.

Google Scholar

Altmetric indicators

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0