Wybrane właściwości geometrycznej struktury powierzchni wytworów porowatych otrzymanych z polietylenu

T. Garbacz; B. Samujło

Published : 2022-08-23

Vol. 53 No. 6 (2008)

Selected properties of geometric structure of the surface of cellular polyethylene products

T. Garbacz B. Samujło

Abstract

The conditions were found in which the cellular topcoats of energetic and installation cables, fulfilling exploitation requirements (as for cables of trademark "OWY 3 x 1.5mm2 450/750 V"), were obtained by foam extrusion (Fig. 1, 2, 4 and 5). The topcoats were made of two commercial grades of PE-HD polyethylene, produced by Borealis (Table 1). Polyethylene was mixed with blowing agent "Hydrocel 530" in amounts up to 1 wt. %. The effects of blowing agent content on mean density, porosity degree (Table 2) and the roughness parameters of the surface were evaluated. Roughness parameters studied were as follows: mean arithmetic deviation of surface roughness profile (Ra), ten-point height of irregularities (Rz), maximum peak to valley height (Rm) and mean spacing of irregularities (Sm) (Table 3 and 4). Dependence of (Ra) and (Rz) on blowing agent content has been described with regression equations (Table 5). The values of correlation factors obtained (rkw>0.985) confirmed the good agreement of selected mathematical model with experimental data.

Keywords

wytłaczanie porujące ; polietylen dużej gęstości ; środki porujące ; parametry porowatości foam extrusion ; high-density polyethylene ; blowing agents ; roughness parameters

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Garbacz, T., & Samujło, B. (2022). Selected properties of geometric structure of the surface of cellular polyethylene products. Polimery, 53(6), 471–476. Retrieved from https://polimery.ichp.vot.pl/index.php/p/article/view/1332

References

Sikora R.: „Przetwórstwo tworzyw wielkocząsteczkowych”, Wydawnictwo Edukacyjne, Warszawa 1993, str. 164--166.

2. Sikora R.: ”Podstawy przetwórstwa tworzyw wielkocząsteczkowych”. Wydawnictwo Uczelniane Politechniki Lubelskiej, Lublin 1992, str. 292--307.

3. Sikora R.: Polimery 1996, 41, 694.

4. Bieliński M.: „Techniki porowania tworzyw termoplastycznych”, Wydawnictwo Uczelniane Akademii Techniczno-Rolniczej w Bydgoszczy, 2004, str. 67--78.

5. Zgłosz. pat. RP 376 808 (2006).

6. Zgłosz. pat. RP 381 696 (2007).

7. Tor A.: „The characteristics of cellular extrusion process”, 9th International Symposium of Student and Young Mechanical Engineers, Advances in Mechanical Engineering, Gdańsk 2006.

8. Garbacz T., Samujło B., Jachowicz T.: ”Foaming of extruded layers of telecommunication cables using endothermal foaming agents”. 21st Annual Meeting of The Polymer Processing Society, Lipsk 2005, mat. konf. str. 281.

9. Garbacz T.: „Wybrane charakterystyki procesu wytłaczania porującego”, Teka Komisji Budowy i Eksploatacji Maszyn, Elektronarzędzi, Budownictwa, Oddział PAN w Lublinie, Lublin 2003, str. 129.

10. Garbacz T.: “Processing and selected properties of modified cellular polyethylene”, The Polymer Processing Society. Regional Meeting 2003, Ateny 2003, mat. konf. str. 224.

11. Stasiek A., Łubkowski D., Dzwonkowski J., Szumski Z.: Przetwórstwo Tworzyw 2005, 11, 144.

12. Sikora J. W.: Polimery 2006, 51, 285.

13. Klepka T.: Polimery 2004, 49, 123.

14. Samujło B., Sikora J.W., Kowalska B.: Przetwórstwo Tworzyw 2005, 11, 179.

15. Sikora.W., Samujło B., Kowalska B.: Przetwórstwo Tworzyw 2006, 12, 4.

16. Simonik J.: “Simulation of chemical foaming of polymers”. The Polymer Processing Society, Sixteenth Annual Meeting, Shanghai 2000, mat. konf. str. 276.

17. Tor A.: Eksploatacja i Niezawodność 2005, 2, 18.

18. Praca zbiorowa: „Przetwórstwo tworzyw polimerowych. Podstawy logiczne, formalne i terminologiczne” (red. Sikora R.), Wydawnictwo Politechniki Lubelskiej, Lublin 2006, str. 325--341 i 418--431.

19. Sikora R., Garbacz T., Kowalska B.: „The new calibration-cooling system”, The 4th International Conference on Machining and Measurements of Sculptured Surfaces, Kraków 2006, mat. konf. str. 309.

20. Garbacz T., Tor A.: „Aspekty wytwarzania oraz właściwości wytworów porowanych otrzymanych w procesie wytłaczania”. Zeszyty Naukowe nr 246, Chemia i Technologia Chemiczna, XI Profesorskie Warsztaty Naukowe, Przetwórstwo tworzyw polimerowych, Bydgoszcz 2006, str. 37.

21. Garbacz T., Tor A.: Polimery 2007, 52, 286.

22. Maciaszek St.: Chemik 1980, 33, 11.

23. Benkreira H., gale M., Patel R. i współpr.: Int. Polym. Process. 2004, 19, 111.

24. Garbacz T., Tor A.: “Characteristics of producing cellular products in the extrusion process”. International Conference on Polymer Processing, ICPP, Pekin 2007, 129.

25. Garbacz T.: Polimery 2004, 49, 23.

26. Garbacz T.: Int. Polym. Sci. Technol. 2004, 31, 8.

27. Greń J.: „Statystyka matematyczna. Modele i zadania”, PWN, Warszawa 1982, str. 35-- 52.

28. Polański Z.: „Planowanie doświadczeń w technice”, PWN, Warszawa 1984 , str. 33-- 47.

Google Scholar

Altmetric indicators

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0