Wpływ budowy chemicznej kopolimerów poli(uretanowo-siloksanowych) na wartości swobodnej energii powierzchniowej powłok z nich otrzymywanych

P. Król; Ł. Byczyński

Published : 2022-08-23

Vol. 53 No. 11-12 (2008)

Influence of chemical structure on the values of free surface energy of the coatings made of poly(urethane-siloxane) copolymers

P. Król Ł. Byczyński

Abstract

Segmental poly(urethane-siloxane) (PUR-PDMS) copolymers were prepared by two-stage (prepolymer) method. In the first stage a polyaddition of 4,4'-diphenylmethane diisocyanate (MDI, rigid segments) with poly(oxytetramethylene) glycol (PTMG, soft segments) was carried in mass. In the following batches PTMG was replaced - in the wide range of amount - with ?,?-di(hydroxyethyleneoxypropylene) poly(dimethylsiloxane) (PDMS, soft segments) (Table 1). At the next stage the chain of prepared isocyanate prepolymer was extended with 1,4-butanediol (BD, soft segment). In this way a series of PUR-PDMS copolymers, differing in chemical structure (confirmed by IR analysis, Fig. 1-3) but containing the same part of soft segments (63 wt. %) and of increasing hydrophobicity, was synthesized. An interpretation of IR spectra has been done applying the intensities of selected bands for quantitative evaluation of copolymers' compositions and to characterize the polarity of the structures obtained, using specially defined structural parameter ?p (Table 3-5). The values of surface free energy (SEP) and its components were determined, using van Oss-Chauhury-Good's model, on the basis of contact angle (?) measurements for three standard liquids (Table 2). It was found that introduction of PDMS segments to the linear chain of PUR polymer caused decrease in SEP and the main role played the polar component (Table 6).

Keywords

segmentowe poliuretany ; kopolimery poli(uretanowo-siloksanowe) ; budowa chemiczna ; widma IR ; swobodna energia powierzchniowa ; model van Ossa-Chauhury'ego-Gooda ; polarność struktur ; hydrofobowość segmental polyurethanes ; poly(urethane-siloxane) copolymers ; chemical structure ; IR spectra ; surface free energy ; van Oss-Chauhury-Good's model ; structure polarity ; hydrophobicity

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Król, P., & Byczyński, Ł. (2022). Influence of chemical structure on the values of free surface energy of the coatings made of poly(urethane-siloxane) copolymers. Polimery, 53(11-12), 808–816. Retrieved from https://polimery.ichp.vot.pl/index.php/p/article/view/1370

References

Król R, Byczyński Ł.: Przem. Chem. 2007, 86,643.

2. Król R: Próg. Mater. Sci. 2007, 52,915.

3. Król R, Król B.: Eur. Ceram. Soc. 2006,26,2241.

4. Chen K.-Y., Kuo J.-E, Chen Ch.-Y.: Biomaterials 2000, 21,161.

5. Rościszewski R, Zielecka M.: „Silikony właściwości i zastosowanie", WNT, Warszawa 2002.

6. Briganti E., Łosi R, Raffi A., Scotcianti M., Munao A., Soldani G.: /. Mater Med. 2006,17,259.

7. Yaidya A., Chaudhurry K.: Colloid Interface Sci 2002,249,235.

8. Belva E, Bourbigot S., Duąuesne S., Jama C., Le Bras M., Pelegris C., Rivenet M.: Polym. Adv. Technol 2006, 17,304.

9. Li C.-Y, Chen J.-H., Chien R-C, Chiu W.-Y, Chen R-S., Don T.-M: Polym. Eng. Sci. 2007,47,625.

10. Chen H., Fan Q., Chen D., Yu X.: Appl Polym. Sci. 2001,79,295.

11. Fan Q., Fang J., Chen Q., Yu X.: Appl Polym. Sci. 1999,74,2552.

12. Chen R. S., Chang C. J., Chang Y H.: Polym. Sci. Parł A 2005,43,3482.

13. Khorasami M. T., Moemen Bellah S., Mirzadeh H., Sadatnia B.: Colloids Surf. B 2006, 51,112.

14. Goddard J. M., Hotchkiss J. H.: Próg. Polym. Sci. 2007, 32,698.

15. Kumar R.: Polimery 2007, 52,336.

16. Rudawska A., Zajchowski S.: Polimery 2007,52,453.

17. Kopczyńka A., Ehrenstein G. W.: Polimery 2007, 52, 666.

18. Stagg H. E.: The Analyst 1966,71,557.

19. Good J. R.: „Fundamentals of Adhesion", Dekker, New York 1991, str. 153.

20. Żenkiewicz M.: „Modyfikowanie warstwy wierzchniej tworzyw wielkocząsteczkowych", WNT, Warszawa 2000.

21. van Oss C. J.: Chem. Rev. 1988, 88, 927.

22. Żenkiewicz M.: Polimery 2006, 51,169.

23. Żenkiewicz M.: Polimery 2007,52, 760.

24. Król R, Król B.: Polimery 2007, 52,427.

Google Scholar

Altmetric indicators

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0