Niekonwencjonalne sieciowanie mieszanin chlorosulfonowanego polietylenu i karboksylowanego kauczuku butadienowo-akrylonitrylowego

M. Kozioł; W. M. Rzymski

Published : 2022-09-01

Vol. 50 No. 7-8 (2005)

Unconventional crosslinking of the blends of chlorosulfonated polyethylene and carboxylated acrylonitrile-butadiene rubber

M. Kozioł W. M. Rzymski

Abstract

Interpolymeric crosslinking of chlorosulfonated polyethylene/carboxylated acrylonitrile-butadiene rubber blends (CSM/XNBR) (Table 2) with MgO in the presence of stearic acid at temp. 433 K (160 oC) for 30 min has been investigated. Effect of CSM containing various amounts of chlorine bonded (Table 1) on the properties of CSM/XNBR blends was studied as well. Extent of crosslinking was estimated on the basis of determinations of vulcametric torque (L) (Fig. 1), equilibrium swelling (Qv) in selected solvents and sol fraction content (fraction soluble in 2-butanone - S) (Tables 3 and 5). It was found that CSM did not undergo crosslinking in given conditions while in the blend with XNBR the interpolymeric reaction of both elastomers occurred. It was confirmed by bounded chlorine values, S and IR analysis (Fig. 2, Table 4). It was observed that degree of CSM bonding with the network depends on its type and content in the blend. Tensile strength (TSb), elongation at break (Eb) temperature dependence of dynamic loss tangent (tgd) and storage modulus (E') (Fig. 3) were determined using dynamic mechano-thermal analysis (DMTA) of cured CSM/XNBR blends. There were found ionic interpolymeric bonds of structure ~C-CO-O-+Mg+-O-SO2-C~ in cured CSM/XNBR blend [equations (1)-(3)] which gave the blend high mechanical strength and act as chemical compatibilizer.

Keywords

polietylen chlorosulfonowany ; karboksylowany kauczuk butadienowo-akrylonitrylowy ; mieszaniny elastomerów ; sieciowanie ; wiązania interpolimerowe ; właściwości mechaniczne chlorosulfonated polyethylene ; carboxylated acrylonitrile-butadiene rubber ; blends of elastomers ; crosslinking ; interpolymeric bonds ; mechanical properties

Similar Articles

M. Żenkiewicz, K. Moraczewski, P. Rytlewski, M. Stepczyńska, T. Żuk, Characteristic and applications of single polymer composites , Polimery: Vol. 60 No. 1 (2015)
M. Wenda, R. Jeziórska, M. Zielecka, M. Panasiuk, Application of silver nanoparticles in the modification of polymers , Polimery: Vol. 61 No. 3 (2016)
M. Łatwińska, J. Sójka-Ledakowicz, M. Kudzin, Influence of poly(3-hydroxybutyrate) addition on the properties of poly(lactic acid) nonwoven obtained by the melt-blown technique , Polimery: Vol. 60 No. 7-8 (2015)
E. Chmiel-Szukiewicz, Polyurethane foams based on oligoetherols obtained from 6-aminouracil and alkylene carbonates , Polimery: Vol. 55 No. 11-12 (2010)
M. Żenkiewicz, T. Żuk, M. Błaszkowski, Use of response surface methodology in characterization of properties of recycled high density polyethylene/ground tire rubber compositions , Polimery: Vol. 59 No. 6 (2014)
M.J. Suriani, S.M. Sapuan, C.M. Ruzaidi, J. Naveen, H. Syukriyah, M. Ziefarina, Correlation of manufacturing defects and impact behaviors of kenaf fiber reinforced hybrid fiberglass/Kevlar polyester composite , Polimery: Vol. 66 No. 1 (2021)
Z. Staniszewski, A. Piegat, M. Piątek-Hnat, M. El Fray, The effect of catalyst and segmental composition on the crystallization of multiblock polyesters for biomedical applications , Polimery: Vol. 59 No. 7-8 (2014)
Kamila Wiśniewska, Zbigniew Rybak, Marcin Wątrobiński, Marcin H. Struszczyk, Jarosław Filipiak, Maria Szymonowicz, Bioresorbable polymeric materials – current state of knowledge , Polimery: Vol. 66 No. 1 (2021)
D. Sykutera, M. Bieliński, Selected properties of recycled polypropylene obtained from porous injection molded parts , Polimery: Vol. 59 No. 7-8 (2014)
K. Formela, M. Bogucki, P. Stączek, Effect of the conditions of thermomechanical reclaiming of ground tire rubber on the properties of reclaimed rubber materials , Polimery: Vol. 60 No. 1 (2015)

<< < 63 64 65 66 67 68 69 70 71 72 > >>

You may also start an advanced similarity search for this article.

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Kozioł, M., & Rzymski, W. M. (2022). Unconventional crosslinking of the blends of chlorosulfonated polyethylene and carboxylated acrylonitrile-butadiene rubber. Polimery, 50(7-8), 587–592. Retrieved from https://polimery.ichp.vot.pl/index.php/p/article/view/1667

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0

M. Kozioł

Affiliation
Politechnika Łódzka, Instytut Polimerów, ul. Stefanowskiego 12/16, 90-924 Łódź

W. M. Rzymski rzymski@p.lodz.pl

Affiliation
Politechnika Łódzka, Instytut Polimerów, ul. Stefanowskiego 12/16, 90-924 Łódź