Właściwości wysokoudarowego polistyrenu uniepalnionego przy użyciu wodorotlenku magnezu i modyfikowanego trójblokowym kopolimerem styren/butadien/styren

J. Garbarski; M. Fabijański

Published : 2022-09-01

Vol. 50 No. 3 (2005)

Properties of high impact polystyrene flame retarded by magnesium hydroxide and modified with triblock copolymer styrene/butadiene/styrene

J. Garbarski M. Fabijański

Abstract

Mechanical, combustible and smoke properties of two series of high impact polystyrene (PS-HI) compositions differing in the content of flame retardant [Mg(OH)2] and amount of a modifier (SBS) mentioned in the title (Table 1). In the first series of experiments [50 wt. % of Mg(OH)2] it has been found that modification with 15 wt. % of SBS causes significant increase in impact strength (U) (Fig. 1) and decrease in maximum strength (Ru), Young modulus (E) and hardness (HK) (Fig. 2-4). Also oxygen index (OI) deteriorated (Fig. 5). Decreases in values of exposure (S) and illumination at fourth minute (E4) (Fig. 6 and 7) show the increased smoke evolution. In the other series of experiments Mg(OH)2 content was increased up to 55 wt. % and various amounts of SBS were used (4.5, 13.5 or 22.5 wt. %). It was observed that U and Ru increased with SBS content increase (Fig. 8 and 9) while E and HK lowered clearly (Fig. 10 and 11). Increase in modifier amount positively influenced OI (Fig. 12) and improved smoke properties (Fig. 13 and 14). Flame retardant used caused that the plastic did not melt and did not flow as burning drops. None of the samples was burnt despite small thickness (5 mm).

Keywords

polistyren wysokoudarowy ; uniepalnianie ; wodorotlenek magnezu ; kopolimer styren-butadien-styren ; właściwości mechaniczne ; wskaźnik tlenowy ; intensywność dymienia high impact polystyrene ; flame retardation ; magnesium hydroxide ; copolymer styrene/butadiene/styrene ; mechanical properties ; oxygen index ; smoke intensity

Similar Articles

W. Zatorski, Z. K. Brzozowski, K. Łebek, Production of PUR and PUR-PIR foams with red phosphorus as a flame retardant , Polimery: Vol. 50 No. 9 (2005)
A. Prociak, J. Pielichowski, Possibility of application of polyurethane foam wastes for heat-insulating materials preparation , Polimery: Vol. 50 No. 9 (2005)
S. Łabużek, J. Pająk, B. Nowak, Biodegradation of modified polyethylene in soil under laboratory conditions , Polimery: Vol. 50 No. 9 (2005)
A. Smejda-Krzewicka, W. M. Rzymski, Selected properties of elastoionomers prepared by reactive processing , Polimery: Vol. 50 No. 9 (2005)
M. Kozioł, W. M. Rzymski, Unconventional crosslinking of the blends of chlorosulfonated polyethylene and carboxylated acrylonitrile-butadiene rubber , Polimery: Vol. 50 No. 7-8 (2005)
R. Janik, S. Kucharski, Synthesis and properties of photosensitive organic and hybrid (inorganic-organic) polymer materials containing chromophoric diazene moiety , Polimery: Vol. 50 No. 7-8 (2005)
A. Gałęski, E. Piórkowska, M. Pluta, Z. Kuliński, R. Masirek, Modification of physical properties of polylactide , Polimery: Vol. 50 No. 7-8 (2005)
S. Słomkowski, M. Gadzinowski, S. Sosnowski, I. Radomska-Galant, Polylactide containing nanoparticles - new carriers of active compounds , Polimery: Vol. 50 No. 7-8 (2005)
A. Bajorek, J. Kabatc, J. Pączkowski, Application of styrylquinolinium dyes as spectroscopic probes in radical polymerization process , Polimery: Vol. 52 No. 7-8 (2007)
M. M. Zgoda, M. Woskowicz, M. Nachajski, M. K. Kołodziejczyk, M. Lukosek, W. Jerzykiewicz, Surfactants from the group of fatty acids polyethylenated esters. Part II. Basic viscometric values and solubility parameter in relation to hydrophilic-lipophilic balance of the products of oxyethylenation of rape oil fatty acids methyl esters , Polimery: Vol. 50 No. 11-12 (2005)

<< < 101 102 103 104 105 106 107 108 109 110 > >>

You may also start an advanced similarity search for this article.

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Garbarski, J., & Fabijański, M. (2022). Properties of high impact polystyrene flame retarded by magnesium hydroxide and modified with triblock copolymer styrene/butadiene/styrene. Polimery, 50(3), 190–195. Retrieved from https://polimery.ichp.vot.pl/index.php/p/article/view/1706

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0

J. Garbarski polimery@ichp.pl

Affiliation
Politechnika Warszawska, Instytut Technologii Materiałowych, ul. Narbutta 85, 02-524 Warszawa

M. Fabijański

Affiliation
Politechnika Warszawska, Instytut Technologii Materiałowych, ul. Narbutta 85, 02-524 Warszawa