Układ katalityczny "Visico-Ambicat" umożliwiający sieciowanie polietylenu w temperaturze pokojowej

W. Krasowski

Published : 2022-09-19

Vol. 46 No. 10 (2001)

The "Visico-Ambicat" catalytic system enabling polyethylene to be crosslinked at room temperature

W. Krasowski

Abstract

A new catalytic system (VISICO-AMBICAT) allows to eliminate the crosslinking of PE in hot water or in steam as a step in the fabrication of PE-coated low-tension aerial cables. PE can be crosslinked in the presence of moisture at room temperature. As step I, basis PE-VISICO-AMBICAT blends were extruded in a laboratory extruder to produce the strips to be used to measure the mechanical and electrical properties (Tables 1-4). As step II, the blend was used to coat a prototype cable. The cable was tested in compliance with a Branch Standard (Table 5). Results were positive.

Keywords

napowietrzne kable samonośne ; izolacja polietylenowa ; układ katalityczny ; uniepalniacz ; sieciowanie ; Hot Set Test ; mechaniczne właściwości izolacji ; elektryczne właściwości izolacji self-supporting aerial cables ; polyethylene insulation ; catalytic system ; flame retardant ; crosslinking ; Hot Set Test ; mechanical properties of polyethylene coat ; electrical properties of polyethylene coat

Similar Articles

K. Śmiechowski, J. Żarłok, J. Skiba, E. Wardzińska, P. Penczek, Possibility of epoxy resins application in the tanning process , Polimery: Vol. 54 No. 6 (2009)
M. Noryani, S.M. Sapuan, M.T. Mastura, M.Y.M. Zuhri, E.S. Zainudin, Statistical inferences in material selection of a polymer matrix for natural fiber composites , Polimery: Vol. 65 No. 2 (2020)
Mateusz Barczewski, Kinga Biedrzycka, Olga Mysiukiewicz, Danuta Matykiewicz, Jacek Andrzejewski, Arkadiusz Kloziński, Marek Szostak, Milled basalt fibers as reinforcement for polyurea composite spray coatings with improved thermomechanical stability and mechanical performance , Polimery: Vol. 65 No. 3 (2020)
E. Markiewicz, S. Borysiak, D. Paukszta, Polypropylene-lignocellulosic material composites as promising sound absorbing materials , Polimery: Vol. 54 No. 6 (2009)
Tobiasz Gabryś, Czesław Ślusarczyk, Effect of graphene oxide additive on the structure of composite cellulose fibers , Polimery: Vol. 65 No. 9 (2020)
Joanna Paciorek-Sadowska, Marcin Borowicz, Marek Isbrandt, Łukasz Grzybowski, Bogusław Czupryński, The use of biodegradable polymer as an alternative raw material for the production of new ecopolyol , Polimery: Vol. 65 No. 10 (2020)
Daria Kosmalska, Halina Kaczmarek, Rafał Malinowski, Krzysztof Bajer, Advances in studies of thermal degradation of polymeric materials Part II. The influence of various factors on the thermal degradation of polymeric materials during their processing , Polimery: Vol. 64 No. 5 (2019)
Barbara Dach, Marek Bryjak, Jolanta Bryjak, Rafał Łużny, New boron selective sorbents for sorption – membrane hybrid system , Polimery: Vol. 67 No. 4 (2022)
Bartosz Bienias, Wojciech Michalski, Leopold Wagner, Mechanical strength evaluation of poly(methyl methacrylate) reinforced with long glass, carbon and aramid fibers , Polimery: Vol. 64 No. 6 (2019)
Maciej Cader, Małgorzata Zaborniak, Michał Stączek, Accuracy analysis of the CAD models reproduction for polymers parts, produced using additive manufacturing at manufacturing process based on Industry 4.0 convention , Polimery: Vol. 64 No. 6 (2019)

<< < 83 84 85 86 87 88 89 90 91 92 > >>

You may also start an advanced similarity search for this article.

Details

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Krasowski, W. (2022). The "Visico-Ambicat" catalytic system enabling polyethylene to be crosslinked at room temperature. Polimery, 46(10), 704–708. Retrieved from https://polimery.ichp.vot.pl/index.php/p/article/view/2124

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0