Niekonwencjonalne sieciowanie mieszanin chlorosulfonowanego polietylenu i karboksylowanego kauczuku butadienowo-akrylonitrylowego

M. Kozioł; W. M. Rzymski

Published : 2022-09-01

Vol. 50 No. 7-8 (2005)

Unconventional crosslinking of the blends of chlorosulfonated polyethylene and carboxylated acrylonitrile-butadiene rubber

M. Kozioł W. M. Rzymski

Abstract

Interpolymeric crosslinking of chlorosulfonated polyethylene/carboxylated acrylonitrile-butadiene rubber blends (CSM/XNBR) (Table 2) with MgO in the presence of stearic acid at temp. 433 K (160 oC) for 30 min has been investigated. Effect of CSM containing various amounts of chlorine bonded (Table 1) on the properties of CSM/XNBR blends was studied as well. Extent of crosslinking was estimated on the basis of determinations of vulcametric torque (L) (Fig. 1), equilibrium swelling (Qv) in selected solvents and sol fraction content (fraction soluble in 2-butanone - S) (Tables 3 and 5). It was found that CSM did not undergo crosslinking in given conditions while in the blend with XNBR the interpolymeric reaction of both elastomers occurred. It was confirmed by bounded chlorine values, S and IR analysis (Fig. 2, Table 4). It was observed that degree of CSM bonding with the network depends on its type and content in the blend. Tensile strength (TSb), elongation at break (Eb) temperature dependence of dynamic loss tangent (tgd) and storage modulus (E') (Fig. 3) were determined using dynamic mechano-thermal analysis (DMTA) of cured CSM/XNBR blends. There were found ionic interpolymeric bonds of structure ~C-CO-O-+Mg+-O-SO2-C~ in cured CSM/XNBR blend [equations (1)-(3)] which gave the blend high mechanical strength and act as chemical compatibilizer.

Keywords

polietylen chlorosulfonowany ; karboksylowany kauczuk butadienowo-akrylonitrylowy ; mieszaniny elastomerów ; sieciowanie ; wiązania interpolimerowe ; właściwości mechaniczne chlorosulfonated polyethylene ; carboxylated acrylonitrile-butadiene rubber ; blends of elastomers ; crosslinking ; interpolymeric bonds ; mechanical properties

Similar Articles

Alaa Shaban, Salah Mahdi Al-Shukri, Hussein Ismail Kahlaf, Othman A. Al Hanbali, Synthesis, characterization, thermal and fire retardant properties of new homo- and block copolymers of polyacrylate and epoxy resin with cyclotriphosphazene core , Polimery: Vol. 64 No. 9 (2019)
Mariusz Oleksy, Rafał Oliwa, Katarzyna Bulanda, Robert Szałajko, Grzegorz Budzik, Izabela Skrzypczak, Phenol-formaldehyde resin composites filled with modified phlogopite reinforced with hybrid glass and basalt fiber meshes used as grinding wheels , Polimery: Vol. 65 No. 11-12 (2020)
Maria Wiśniewska-Wrona, Mirosława El Fray, Physicochemical and functional properties of polymer biocomposites , Polimery: Vol. 64 No. 1 (2019)
Arkadiusz Klozinski, Mateusz Barczewski, Comparison of off -line, on-line and in-line measuring techniques used for determining the rheological characteristics of polyethylene composites with calcium carbonate , Polimery: Vol. 64 No. 2 (2019)
Krzysztof J. Wilczyński, Kamila Buziak, Simulation of single screw extrusion of wood plastic composites based on the on-line pressure measurements , Polimery: Vol. 64 No. 2 (2019)
Halina Kaczmarek, Daria Kosmalska, Rafał Malinowski, Krzysztof Bajer, Advances in studies of thermal degradation of polymeric materials. Part I. Literature studies , Polimery: Vol. 64 No. 4 (2019)
Arkadiusz Kloziński, Paulina Jakubowska, Joanna E. Przybylska, Robert Przekop, Application of in-line rheological measurements for characterization of polypropylene/opoka rock powder composites , Polimery: Vol. 64 No. 4 (2019)
Daria Kosmalska, Halina Kaczmarek, Rafał Malinowski, Krzysztof Bajer, Advances in studies of thermal degradation of polymeric materials Part II. The influence of various factors on the thermal degradation of polymeric materials during their processing , Polimery: Vol. 64 No. 5 (2019)
Mariusz Oleksy, Joanna Oliwa, Grzegorz Budzik, Rafał Oliwa, Katarzyna Bulanda, Maciej Nędza, The use of a mixer with built-in Parshall’s venturi for modification of bentonite designed for the filling of polymer resins , Polimery: Vol. 64 No. 6 (2019)
Maciej Cader, Małgorzata Zaborniak, Michał Stączek, Accuracy analysis of the CAD models reproduction for polymers parts, produced using additive manufacturing at manufacturing process based on Industry 4.0 convention , Polimery: Vol. 64 No. 6 (2019)

<< < 111 112 113 114 115 116 117 118 119 120 > >>

You may also start an advanced similarity search for this article.

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Kozioł, M., & Rzymski, W. M. (2022). Unconventional crosslinking of the blends of chlorosulfonated polyethylene and carboxylated acrylonitrile-butadiene rubber. Polimery, 50(7-8), 587–592. Retrieved from https://polimery.ichp.vot.pl/index.php/p/article/view/1667

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0

M. Kozioł

Affiliation
Politechnika Łódzka, Instytut Polimerów, ul. Stefanowskiego 12/16, 90-924 Łódź

W. M. Rzymski rzymski@p.lodz.pl

Affiliation
Politechnika Łódzka, Instytut Polimerów, ul. Stefanowskiego 12/16, 90-924 Łódź