Właściwości reologiczne styrenowych elastomerów termoplastycznych modyfikowanych radiacyjnie

D. Żuchowska; W. Meissner; R. Steller

Published : 2022-09-17

Vol. 48 No. 9 (2003)

Rheological properties of radiation modified thermoplastic styrene elastomers

D. Żuchowska W. Meissner R. Steller

Abstract

The results of rheological investigations of triblock copolymers styrene/butadiene/styrene (SBS) and styrene/ethylene-co-butylene/styrene (SEBS), i.e. steady shear viscosity (eta), storage modulus (G') and loss factor (tgdelta) measured at temp. 200 degreesC before and after electron beam irradiation (dose 0, 60 and 100 kGy) were presented. Irradiated and non-irradiated samples were also investigated before and after thermal treatment (60 min at 200 degreesC) in rheometer without shearing. On the basis viscosity, elastic modulus and loss factor changes (Table 1, Figs. 1-7) it has been stated that SBS copolymer is more susceptible to radiation and thermal treatments than SEBS. Both treatments lead to decrease in flowability of SBS and SEBS copolymers with simultaneous increase in their elastic properties. Results of 11, G' and tgdelta measurements were also used for the interpretation of probable molecular structure changes caused by radiation and thermal treatments.

Keywords

blokowy kopolimer styren/butadien/ styren ; blokowy kopolimer styren/(etylen/butylen)/styren ; modyfikacja radiacyjna ; obróbka termiczna ; zmiany strukturalne styrene/butadiene/styrene block copolymer ; styrene/ethylene-co-butylene/styrene block copolymer ; radiation modification ; thermal treatment ; structure changes

Similar Articles

A. Prociak, S. Michałowski, S. Bąk, Thermoplastic polyurethane foamed under microwave irradiation , Polimery: Vol. 57 No. 11-12 (2012)
B. Waśniewski, M. Auguścik, P. Parzuchowski, M. Zielecka, J. Ryszkowska, Polycarbonate urethane nanocomposites with nanosilica for implants of the intervertebral disc , Polimery: Vol. 57 No. 11-12 (2012)
B. Pilch-Pitera, Polyurethane powder lacquers modified with fluorine compounds , Polimery: Vol. 57 No. 11-12 (2012)
B. Pilch-Pitera, J. Wojturska, Biodegradation of poly(ester urethanes) under simulated composting conditions , Polimery: Vol. 57 No. 11-12 (2012)
G. Przybyłek, Synthesis of polyhydroxyalkanates from waste glycerol obtained in the production of biodiesel , Polimery: Vol. 56 No. 2 (2011)
T. Garbacz, Properties of triple-layered pvc coatings synthesized in the micropore coextrusion method , Polimery: Vol. 56 No. 2 (2011)
R. Lubczak, Synthesis of oligoetherols with a carbazole ring and an azo group , Polimery: Vol. 56 No. 2 (2011)
B. Grabowska, M. Holtzer, M. Eichholz, K. Hodor, A. Bobrowski, Thermal analysis of a sodium salt of the maleic acid-acrylic acid copolymer used as a polymeric binder , Polimery: Vol. 56 No. 2 (2011)
S. Kuciel, A. Liber-Kneć, Biocomposites based on PHB filled with wood or kenaf fibers , Polimery: Vol. 56 No. 3 (2011)
A. Wąsicki, A. Kościuszko, DSC investigations of the surface layer of an aged polypropylene/wood composite , Polimery: Vol. 56 No. 5 (2011)

<< < 42 43 44 45 46 47 48 49 50 51 > >>

You may also start an advanced similarity search for this article.

Details

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Żuchowska, D., Meissner, W., & Steller, R. (2022). Rheological properties of radiation modified thermoplastic styrene elastomers. Polimery, 48(9), 620–626. Retrieved from https://polimery.ichp.vot.pl/index.php/p/article/view/1906

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0

D. Żuchowska polimery@ichp.pl

Affiliation
Politechnika Wrocławska, Instytut Technologii Organicznej i Tworzyw Sztucznych, Wybrzeże Wyspiańskiego 27, 50-370 Wrocław, Poland

W. Meissner

R. Steller