Badania wpływu wygrzewania i starzenia promieniami UV na strukturę kompatybilizowanych mieszanin PP/PA 6

A. Gnatowski

Published : 2011-02-28

Vol. 56 No. 2 (2011)

Studies on the influence of soaking and ultraviolet irradiation ageing on the structure of compatibilized PP/PA 6 mixtures

A. Gnatowski

Abstract

The results of investigations on the crystallinity and structure of polypropylene, polyamide 6 and their mixtures have been presented. The mixtures prepared in compositions of 30, 50 and 70 wt. % of polypropylene in relation to the polyamide using polyvinylpyrrolidone (PVP) as compatibilizing agent. The influence of soaking, UV irradiation ageing or both on the crystallinity and structure on polypropylene and polyamide 6 virgin samples, as well as on their mixtures was determined. On the basis of obtained DSC curves and optical microscope images (Table 2, Figs. 1-10), it was concluded, that soaking and UV irradiation caused a significant increase of the crystalline phase in all the studied samples, while the melting temperature range and degree of crystallinity did not change significantly. An increase in the resistance to UV-induced ageing after preliminary soaking of the samples was also observed.

Keywords

poliamid ; polipropylen ; poliwinylopirolidon ; mieszaniny ; starzenie UV ; wygrzewanie ; różnicowa kalorymetria skaningowa ; mikroskopia optyczna polyamide ; polypropylene ; mixtures ; UV ageing ; soaking ; optical microscopy

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Gnatowski, A. (2011). Studies on the influence of soaking and ultraviolet irradiation ageing on the structure of compatibilized PP/PA 6 mixtures. Polimery, 56(2), 121–128. Retrieved from https://polimery.ichp.vot.pl/index.php/p/article/view/899

References

Manning S. C., Moore R. B.: Polym. Eng. Sci. 1999, 39, 1921.

2. Campoy J., Arribas J. M., Zaporta U. M.: Eur. Polym. J. 1995, 31, 475.

3. Pigłowski J. i in.: Polymer 2000, 41, 6813.

4. Tao Y., Mai K.: Eur. Polym. J. 2007, 43, 3538.

5. Wang D., Xie X.: Polymer 2006, 47, 7859.

6. Morawiec J. i in.: Polimery 2004, 49, 52.

7. Chow W. i in.: Polymer 2003, 44, 42.

8. Charoen N. i in.: Polym. Test. 2006, 25, 413.

9. Szymczyk A. i in.: Polimery 1999, 44, 30.

10. Gnatowski A., Koszkul J.: J. Mater. Process. Technol. 2006, 175, 212.

11. González J. i in.: Polym. Degrad. Stab. 2000, 68, 9.

12. Gnatowski A., Koszkul J.: J. Mater. Process. Technol. 2005, 162--163, 52.

13. Pohl D., Newman S.: „Polimiernyje smiesi”, Mir, Moskwa 1981.

14. Sikora R.: „Tworzywa wielkocząsteczkowe. Rodzaje, właściwości i struktura”, Wydawnictwo Politechniki Lubelskiej, Lublin 1991.

15. Żuchowska D.: „Polimery konstrukcyjne”, WNT, Warszawa 2000.

16. Kelar K.: „Modyfikacja polimerów”, Wydawnictwo Politechniki Poznańskiej, Poznań 1992.

17. Buckton G. i in.: Int. J. Pharm. 2006, 312, 61.

18. Cyntia A. i in.: Pharm. Res. 1990, 7, 654.

19. Menyhárd A., Varga J.: Eur. Polym. J. 2006, 42, 3257.

20. Gnatowski A.: J. Polym. Eng. 2007, 27, 507.

21. Koszkul J.: Polimery 1999, 44, 255.

22. Fouda I. M., Oraby A. H.: Polym. Test. 1999, 18, 235.

23. Gnatowski A., Koszkul J.: J. Polym. Eng. 2005, 25, 149.

24. El-Nouby M., El Shazly M.: Atmos. Environ. 2007, 41, 4856.

25. Medhaug I., Olseth J., Reuder J.: J. Photochem. Photobiol. B: Biology 2009, 96, 232.

26. João F. i in.: Appl. Energy 2009, 86, 299.

27. Samy A.: Energy Convers. Manag. 2008, 49, 2384.

Google Scholar

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0