Właściwości wysokoudarowego polistyrenu uniepalnionego przy użyciu wodorotlenku magnezu i modyfikowanego trójblokowym kopolimerem styren/butadien/styren

J. Garbarski; M. Fabijański

Published : 2022-09-01

Vol. 50 No. 3 (2005)

Properties of high impact polystyrene flame retarded by magnesium hydroxide and modified with triblock copolymer styrene/butadiene/styrene

J. Garbarski M. Fabijański

Abstract

Mechanical, combustible and smoke properties of two series of high impact polystyrene (PS-HI) compositions differing in the content of flame retardant [Mg(OH)2] and amount of a modifier (SBS) mentioned in the title (Table 1). In the first series of experiments [50 wt. % of Mg(OH)2] it has been found that modification with 15 wt. % of SBS causes significant increase in impact strength (U) (Fig. 1) and decrease in maximum strength (Ru), Young modulus (E) and hardness (HK) (Fig. 2-4). Also oxygen index (OI) deteriorated (Fig. 5). Decreases in values of exposure (S) and illumination at fourth minute (E4) (Fig. 6 and 7) show the increased smoke evolution. In the other series of experiments Mg(OH)2 content was increased up to 55 wt. % and various amounts of SBS were used (4.5, 13.5 or 22.5 wt. %). It was observed that U and Ru increased with SBS content increase (Fig. 8 and 9) while E and HK lowered clearly (Fig. 10 and 11). Increase in modifier amount positively influenced OI (Fig. 12) and improved smoke properties (Fig. 13 and 14). Flame retardant used caused that the plastic did not melt and did not flow as burning drops. None of the samples was burnt despite small thickness (5 mm).

Keywords

polistyren wysokoudarowy ; uniepalnianie ; wodorotlenek magnezu ; kopolimer styren-butadien-styren ; właściwości mechaniczne ; wskaźnik tlenowy ; intensywność dymienia high impact polystyrene ; flame retardation ; magnesium hydroxide ; copolymer styrene/butadiene/styrene ; mechanical properties ; oxygen index ; smoke intensity

Similar Articles

Jinyong Sui, zhengu, Xiaoyi Zhang, Zhenxu Li, Lining Song, Lina Yang, Ning Wang, Effects of carbon nanotubes and graphene on the structure and properties of natural rubber , Polimery: Vol. 66 No. 4 (2021)
M. Jurewicz, Regulatory frameworks for nanotechnology applications in the production of food-contact plastic materials and articles , Polimery: Vol. 62 No. 2 (2017)
K. Formela, M Cysewska, J. Haponiuk, The influence of materials dosing order and shear forces on the properties of high density polyethylene/ground tire rubber blends obtained in co-rotating twin screw extruder , Polimery: Vol. 59 No. 4 (2014)
Mateusz Barczewski, Jacek Andrzejewski, Danuta Matykiewicz, Agnieszka Krygier, Arkadiusz Kloziński, Influence of accelerated weathering on mechanical and thermomechanical properties of poly(lactic acid) composites with natural waste filler , Polimery: Vol. 64 No. 2 (2019)
O. Gencel, W. Brostow, G. Martínez-Barrera, M. S. Gok, Mechanical properties of polymer concretes containing different amount of hematite or colemanite , Polimery: Vol. 57 No. 4 (2012)
J. Stasiek, E. Piórkowska, A. Gałęski, The influence of blowing extrusion process of PA film on its structure and physical properties , Polimery: Vol. 48 No. 3 (2003)
M. Żenkiewicz, J. Richert, A. Różański, Effects of blow molding ratio on mechanical properties of polylactide nanocomposite films , Polimery: Vol. 55 No. 11-12 (2010)
D. Żuchowska, W. Meissner, R. Steller, Rheological properties of radiation modified thermoplastic styrene elastomers , Polimery: Vol. 48 No. 9 (2003)
M. Barczewski, M. Szostak, D. Nowak, A. Piasecki, Effect of wood flour addition and modification of its surface on the properties of rotationally molded polypropylene composites , Polimery: Vol. 63 No. 11-12 (2018)
Rafał Oliwa, Katarzyna Bulanda, Mariusz Oleksy, Paulina Ostyńska, Grzegorz Budzik, Magdalena Płocińska, Sławomir Krauze, Fire resistance and mechanical properties of powder-epoxy composites reinforced with recycled glass fiber laminate , Polimery: Vol. 65 No. 4 (2020)

1 2 3 4 5 6 7 8 9 10 > >>

You may also start an advanced similarity search for this article.

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Garbarski, J., & Fabijański, M. (2022). Properties of high impact polystyrene flame retarded by magnesium hydroxide and modified with triblock copolymer styrene/butadiene/styrene. Polimery, 50(3), 190–195. Retrieved from https://polimery.ichp.vot.pl/index.php/p/article/view/1706

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0

J. Garbarski polimery@ichp.pl

Affiliation
Politechnika Warszawska, Instytut Technologii Materiałowych, ul. Narbutta 85, 02-524 Warszawa

M. Fabijański

Affiliation
Politechnika Warszawska, Instytut Technologii Materiałowych, ul. Narbutta 85, 02-524 Warszawa