Polyurethane ionomers. Part II. Preparation, structure, properties and applications of polyurethane cationic dispersions

P. Król B. Król

Abstract

Urethane-isocyanate prepolymers have been synthesized in reactions of 1,4- or 2,6-tolylene diisocyanate (TDI) with various polyols. Then tertiary N-alkyl groups were introduced into prepolymers, in reaction with N-butyl- or N-methyldiethaneamine, and the products were protonated with HCOOH to obtain polyurethane cationomers with ammonia groups. Selected cationomer underwent reaction with 2-hydroxyethyl acrylate (HEA) to appropriate macrocationomer (Table 1). 1H NMR and IR spectra presented (Figs. 1-4, Table 2) confirm the expected structures of selected cationomer as well as of macrocationomer. Significant polydispersity of the products has been found using GPC measurements (Fig. 5, Table 3) what was interpreted as coming from the process of synthesis of several stages. Particle size distributions of aqueous dispersions obtained were determined (Fig. 6, Table 4). Contact angle values have been determined as well. Hardness (Fig. 7) and abrasion (Fig. 8) of the coatings, obtained from the dispersions prepared, were determined. On this basis the dispersion of macrocationomer prepared from TDI, oligo(oxyethylenecaprolactono)diol and HEA has been chosen as optimal system suitable for water-soluble varnishes' preparation.

Keywords

kationomery poliuretanowe ; makrokationomery uretanowo-akrylowe ; dyspersje lakiernicze ; rozkład wymiarów cząstek ; kąt zwilżania ; twardość ; ścieralność polyurethane cationomers ; urethane - acrylic macrocationomers ; varnish dispersions ; particle size distribution ; contact angle ; hardness ; abrasion

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Król, P., & Król, B. (2022). Polyurethane ionomers. Part II. Preparation, structure, properties and applications of polyurethane cationic dispersions. Polimery, 49(9), 615–622. Retrieved from https://polimery.ichp.vot.pl/index.php/p/article/view/1792

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0

P. Król polimery@ichp.pl

Affiliation
Politechnika Rzeszowska, Zakład Technologii Tworzyw Sztucznych, ul. Powstańców Warszawy 6, 35-959 Rzeszów

B. Król

Affiliation
Politechnika Rzeszowska, Zakład Technologii Tworzyw Sztucznych, ul. Powstańców Warszawy 6, 35-959 Rzeszów